Hanwei Wang#, Jinzhou Fu#, Chao Wang, Jiangyan Wang, Ankun Yang, Caicai Li, Qingfeng Sun*, Yi Cui*, Huiqiao Li*, A binder-free high silicon content flexible anode for Li-ion batteries, Energy & Environmental Science 2020, 13, 848-858.
https://doi.org/10.1039/C9EE02615K.
Abstract: Despite the high theoretical capacity of Si anodes, their huge volume change and poor electrical connectivity must be overcome by decreasing the feature sizes of the Si particles to the nanoscale and compositing them with highly conductive carbon materials. To ensure the mechanical integrity of the electrodes with uniform dispersion and good electrical contact of the nano-silicon, the industry has to use a relatively low amount of Si (o15% by mass) in commercial anodes. Such a low Si content severely weakens the capacity advantage of silicon at the electrode level. Here, we designed a cellulose-based topological microscroll by the self-rolling of cellulose nanosheets to form a binder-free, flexible, and free-standing electrode comprising an unprecedented 92% silicon content. In the microscroll, carboncoated silicon nanoparticles are anchored on conductive carbon nanotubes and subsequently confined in cellulose carbon rolls with enough internal voids to accommodate the volume expansion of silicon; thus, a uniform dispersion of silicon with high reactivity was achieved. This structure shows an ultrahigh electrode-specific capacity of 2700 mA h g1, excellent cycling stability under a high silicon content of 85% (42000 mA h g1 after 300 cycles) and a commercial-level areal capacity (5.58 mA h cm2). This strategy offers a new way to design electrodes with a high active material content for high performance batteries.